PE/PVDF Coated Aluminum Coil for ACP (1060, 1100, 3003)

Price:
Negotiable
minimum:
Total supply:
Delivery term:
The date of payment from buyers deliver within days
seat:
Henan
Validity to:
Long-term effective
Last update:
2017-12-17 23:27
Browse the number:
217

Send an inquiries

Company Profile

Wuxi Taixie Metal Material Co., Ltd.

By certification [File Integrity]

Contact：Mr. Alex Liu(Mr.)

Email：

Telephone：

Area：Henan

Address：Henan

Website： http://signialuminium.jssytm.com/

Product details

PE/PVDF coated aluminum coil for ACP (1060, 1100, 3003)

Signi PVDF color coated aluminum coil with good PVDF paints and high performance of aluminum coil is produced by advanced roller coating. Florin atom had biggest electro negative performance and it can form a stable high bonding F-C, furthermore, it has special symmetry molecule structure.

Specification of coated aluminum coil
Alloy:1060, 1100, 3003
Temper:HO,H12,H14,H16,H18,H22,H24,H26
Thickness:0.2mm-6.0mm
Width:80mm-2300mm
Standard production:ASTM-B-209M,BS EN 485-2,BS EN 573-3,GB/T3880-2008
Mother coil:DC or CC
ID:76mm,152mm,408mm,508mm
Surface:Color Coated, Many kinds of Color
Package:Export standard package with wooden pallet
Package way:Eye to sky or eye to wall

The coated aluminum coil for ACP

TOP COATING:

TEST	METHOD	RESULTS
Coating nature		PVDF	Standard PE
Thickness	ECCA T1	Color:20±2um Primer:5+2um or according spec.	Color:18-2±2um, or according spec.
Specular Gloss	ECCA T2	Standard ±5%	Standard ±5%
Color difference	ECCA T3	⊿E<1(Non-metallics colors)	⊿E<1(Non-metallics colors)
Polimerization	ILA-06	>100 DF	>100 DF
Pencil Hardness	ECCA T4	≥F	≥F
Impact	ECCA T5	100%	100%
Adhesion (Cross cutting+Erichsen)	ECCA T6	>75%	>75%
Bending	ECCA T7	≤2T	≤2T
Resistant to salt acetic acid spray test	ECCA T8	1000h/class 3 (According to EN1396/C 6.5)(Depends on specification)	1000h/Class 1(According to EN 1396/C.6.5)
Water immersion resistance	ECCA T9	1000h-B2S2	--
Resistance to QUVB test	ECCA T10	10 00 h Gloss Retention ≥90% ⊿E≤2	500h Gloss Retention ≥30% ⊿E≤5
Florida test		Class 3 (According to EU1396/C 6.3)	Class 3 (According to EU1396/C 6.3)

BACK COATING:

TEST	METHOD	RESULT
Thickness coating	ECAA T1	5±2um
Bending	ECAA T7	≤2T
Polimerization	ILA 06	>100 double roubs
Adhesion after cross cutting	ECAA T6	OK
Adhesion after Erichsen	ECAA T6	OK
Resistance to Salt Spray	ECAA T8	1000 hours

Back coat epoxy blue:
Good adhesion to adhesive and PU foam.
Good resistance to corrosion.
Back coat epoxy grey:
Good adhesion to PE(composite panel)
Good resistance to corrosion